| Item | Standard | Data | Units |
| Color | - | Natural | |
| Density | ISO 1138 | 1.3±0.01 | g/cm3 |
| Water Absorption (25℃.24Hrs) | ISO 62 | 0.05 % | |
| Melting temperature | ISO 11357 | 343 | ℃ |
| Distortion Temperature | ISO 75-1/-2 | 163 | ℃ |
| Continuous service Temperature | UL 74685 | 260 | ℃ |
| Thermal expansion coefficient | ASTM D696 | 4.7*10-6 | /K |
| Tensile Strength (23℃) | ISO 527 | 100 | MPa |
| Tensile modulus (23℃) | ISO 527 | 3.8 | GPa |
| Tensile Elongation (23℃) | ISO 527 | 27 % | |
| Bending Strength (23℃) | ISO 178 | 163 | MPa |
| Bending Modulus (23℃) | ISO 178 | 3.5 | GPa |
| Impact Strength(23℃) | ISO 604 | 123 | MPa |
| Lzod Impact Strength (No notched) | ISO 180/U | No Break | kJ/m2 |
| Poisson Ratio | ISO 527-2 | 0.4 | |
| Rockwell Hardness | GB3398.2 | 118 | |
| Flammability | UL 94 (1.5 mm) | V-0 | |
| Dielectric strength | IEC 60243-1 | 18 | KV/mm |
| Dielectric constant | IEC 60250 | 3.2 | |
| Thermal Conductivity | ISO 22007 | 0.28 | W/（m·K） |
| Surface Resistance | IEC 90093 | 1015 | Ω |
| Item | Standard | Data | Units |
| Color | - | Black | |
| Density | ISO 1138 | 1.4±0.03 | g/cm3 |
| Water Absorption (25℃.24Hrs) | ISO 62 | 0.05 % | |
| Melting temperature | ISO 11357 | 343 | ℃ |
| Distortion Temperature | ISO 75-1/-2 | 315 | ℃ |
| Continuous service Temperature | UL 74685 | 260 | ℃ |
| Thermal expansion coefficient | ASTM D696 | 1.5*10-6 | /K |
| Tensile Strength (23℃) | ISO 527 | 125 | MPa |
| Tensile modulus (23℃) | ISO 527 | 9.3 | GPa |
| Tensile Elongation (23℃) | ISO 527 | 2.5 % | |
| Bending Strength (23℃) | ISO 178 | 271 | MPa |
| Bending Modulus (23℃) | ISO 178 | 9.1 | GPa |
| Impact Strength(23℃) | ISO 604 | 196 | MPa |
| Lzod Impact Strength (No notched) | ISO 180/U | 38 | kJ/m2 |
| Poisson Ratio | ISO 527-2 | 0.35 | |
| Rockwell Hardness | GB3398.2 | 123 | |
| Flammability | UL 94 (1.5 mm) | V-0 | |
| Dielectric strength | IEC 60243-1 | - | KV/mm |
| Dielectric constant | IEC 60250 | - | |
| Thermal Conductivity | ISO 22007 | 0.95 | W/（m·K） |
| Surface Resistance | IEC 90093 | 105 | Ω |
| Item | Standard | Data | Units |
| Color | - | Natural | |
| Density | ISO 1138 | 1.5±0.01 | g/cm3 |
| Water Absorption (25℃.24Hrs) | ISO 62 | 0.05 % | |
| Melting temperature | ISO 11357 | 343 | ℃ |
| Distortion Temperature | ISO 75-1/-2 | 315 | ℃ |
| Continuous service Temperature | UL 74685 | 260 | ℃ |
| Thermal expansion coefficient | ASTM D696 | 2.2*10-6 | /K |
| Tensile Strength (23℃) | ISO 527 | 110 | MPa |
| Tensile modulus (23℃) | ISO 527 | 7.9 | GPa |
| Tensile Elongation (23℃) | ISO 527 | 3.5 % | |
| Bending Strength (23℃) | ISO 178 | 214 | MPa |
| Bending Modulus (23℃) | ISO 178 | 7.5 | GPa |
| Impact Strength(23℃) | ISO 604 | 142 | MPa |
| Lzod Impact Strength (No notched) | ISO 180/U | 41 | kJ/m2 |
| Poisson Ratio | ISO 527-2 | 0.35 | |
| Rockwell Hardness | GB3398.2 | 122 | |
| Flammability | UL 94 (1.5 mm) | V-0 | |
| Dielectric strength | IEC 60243-1 | 17 | KV/mm |
| Dielectric constant | IEC 60250 | 3.4 | |
| Thermal Conductivity | ISO 22007 | 0.31 | W/（m·K） |
| Surface Resistance | IEC 90093 | 1015 | Ω |
| Item | Standard | Data | Units |
| Color | - | Black | |
| Density | ISO 1138 | 1.44±0.05 | g/cm3 |
| Water Absorption (25℃.24Hrs) | ISO 62 | 0.05 % | |
| Melting temperature | ISO 11357 | 343 | ℃ |
| Distortion Temperature | ISO 75-1/-2 | 315 | ℃ |
| Continuous service Temperature | UL 74685 | 260 | ℃ |
| Thermal expansion coefficient | ASTM D696 | 2.4*10-6 | /K |
| Tensile Strength (23℃) | ISO 527 | 70 | MPa |
| Tensile modulus (23℃) | ISO 527 | 4.0 | GPa |
| Tensile Elongation (23℃) | ISO 527 | 2.5 % | |
| Bending Strength (23℃) | ISO 178 | 100 | MPa |
| Bending Modulus (23℃) | ISO 178 | 4.0 | GPa |
| Impact Strength(23℃) | ISO 604 | 135 | MPa |
| Lzod Impact Strength (No notched) | ISO 180/U | 26 | |
| Poisson Ratio | ISO 527-2 | 0.35 | |
| Rockwell Hardness | GB3398.2 | 120 | |
| Flammability | UL 94 (1.5 mm) | V-0 | |
| Dielectric strength | IEC 60243-1 | - | KV/mm |
| Dielectric constant | IEC 60250 | - | |
| Thermal Conductivity | ISO 22007 | 0.86 | W/（m·K） |
| Surface Resistance | IEC 90093 | 105 | Ω |
| Thickness | Thickness Tolerance | Fromat | Weight per 1000mm （kg） |
| 1 | -0，+0.1 | 650*1000/3000 | 0.96 |
| 2 | -0，+0.2 | 650*1000/3000 | 1.83 |
| 3 | -0，+0.2 | 650*1000/3000 | 2.78 |
| 4 | -0，+0.3 | 650*1000/3000 | 3.74 |
| 5 | -0，+0.8 | 1250*1000/3000 | 8.8 |
| 6 | -0，+0.8 | 1250*1000/3000 | 11.28 |
| 8 | -0，+0.8 | 1250*1000/3000 | 14.3 |
| 10 | -0，+1 | 1250*1000/3000 | 17.9 |
| 12 | -0，+1 | 1250*1000/3000 | 21.4 |
| 15 | -0，+1 | 1250*1000/3000 | 26.28 |
| 16 | -0，+1 | 1250*1000/3000 | 28.3 |
| 18 | -0，+1 | 1250*1000/3000 | 31.34 |
| 20 | -0，+1.2 | 1250*1000/3000 | 35.3 |
| 22 | -0，+1.2 | 1250*1000/3000 | 38.4 |
| 25 | -0，+1.2 | 1250*1000/3000 | 43.8 |
| 28 | -0，+1.2 | 1250*1000/3000 | 48.5 |
| 30 | -0，+1.5 | 1250*1000/3000 | 52.3 |
| 35 | -0，+1.5 | 1250*1000/3000 | 60.65 |
| 40 | -0，+2 | 1250*1000/3000 | 69.3 |
| 45 | -0，+2 | 1250*1000/3000 | 78.35 |
| 50 | -0，+3 | 1250*1000/3000 | 87.6 |
| 55 | -0，+3 | 1250*1000/3000 | 96.1 |
| 60 | -0，+3 | 1250*1000/3000 | 104.4 |
| 70 | -0，+3 | 1250*1000/3000 | 121.3 |
| 80 | -0，+3 | 1250*1000/3000 | 138.9 |
| 90 | -0，+3 | 1250*1000/3000 | 155.8 |
| 100 | -0，+4 | 1250*1000/3000 | 174.4 |