PEEK 30% Carbon Fiber Reinforced (PEEK5600CF30-GQ) Granules
As an advanced special engineering plastic, PEEK plays an important role in weight reduction, effectively extending the service life of components, and optimizing component utilization due to its good machinability, flame retardant, non-toxic, wear resistance, corrosion resistance, etc., and the promotion of downstream applications is accelerating.
PEEK5600CF30-GQ Granules are an enhanced version based on PEEK5600CF30 (ordinary PEEK carbon fiber modified reinforcement material), a PEEK composite material with 30% carbon fiber modification, which can be produced and processed by injection molding and extrusion. It has higher mechanical strength and dimensional stability than pure PEEK, and its mechanical properties are generally enhanced by more than 12%, which is suitable for extending the service life of parts and reducing the frequency of replacement under harsh conditions such as high load, high wear, and high temperature that PEEK5600CF30 cannot meet the requirements.
| Test items | Test standards or instruments | unit | PEEK5600CF30-GQ |
|---|---|---|---|
| Mechanical properties | |||
| Tensile strength (23℃) | ISO 527-2/1B/50 | MPa | 260 |
| Tensile modulus (23℃) | ISO 527-2/1B/51 | GPa | 24 |
| Elongation at break (23℃) | ISO 527-2/1B/50 | % | 5 |
| Bending strength (23℃) | ISO 178 | MPa | 390 |
| Flexural modulus (23°C) | ISO 178 | GPa | 16 |
| Compression strength (23℃) | ISO 604 | MPa | / |
| Simple supported beam impact strength (unnotched) | ISO 179/U | KJ/m 2 | 45 |
| Izod impact strength (notched) | ISO 180/A | KJ/m 2 | 9 |
| Thermal performance | |||
| Melting point | DSC | ℃ | 343 |
| Heat deformation temperature | ISO 75-1/-2 | ℃ | 335 |
| Continuous use temperature | UL 746B | ℃ | 260 |
| Coefficient of thermal expansion | ASTM D696 | ppm K-1 | 5 |
| Flammability rating | UL 94 | / | V-0 |
| Thermal conductivity | ISO 22007 | W/（m ·K） | 0.95 |
| Electrical properties | |||
| Dielectric strength | IEC 60243-1 | KV/mm | / |
| Dielectric constant | IEC 60250 | – | / |
| Volume resistivity | IEC 60093 | Oh cm | 105 |
| Lossy dielectric | IEC 60251 | – | / |
| Other performance | |||
| color | – | black | |
| Actual density | ISO 1183 | g/cm 3 | 1.40 |
| Water absorption rate (25℃.24Hrs) | ISO 62 | % | 0.05 |
| Molding shrinkage (25-24℃) | 3mm thickness, 170°C flow direction |
% | 1.0 |
| Perpendicular to the flow direction | % | 1.3 | |
| Poisson’s ratio | ISO 527-2 | 0.4 | |
| Rockwell hardness | ISO 2039.2 | 80 | |
| Friction coefficient | ASTM D3702 | m | 0.30-0.35 |
| Melt index | ISO 1133 | g/10min | 10 |
1. Typical values are injection molding specifications. Please contact our technical department for more detailed specifications if necessary.
2. These performance indicators cannot be used as material acceptance criteria.
Contact Us
What is PEEK？
PEEK and its modified composite materials show excellent performance under high temperature and high humidity conditions. PEEK have excellent chemical corrosion resistance, self-lubricating, and wear-resistant properties, so it has become the most ideal material to replace copper alloys and ordinary rubber. Compared with them, PEEK has longer service life which can reduce equipment operating costs, improve equipment operating reliability.
High Temperature Performance
PEEK’s performance can remain stable in the temperature range from -196°C to 260°C. Under extreme working conditions, it can withstand 300″C for a short time. The performance of PEEK is still reliable even in high temperatures of several kilometers underground work environment.
High Strength and Wear Resistance
Compared with other plastics, PEEK is resistant to compression, impact and also have good fatigue resistance. PEEK is durable in mechanical equipment and wear-resistant environments.
Double the Service Life
PEEK sealing solutions can improve the part service life. Some domestic chemical companies use the PEEK5600FE20 polytetrafluoroethylene modified material designed by JUNHUA PEEK to replace the original material, the service life of the wear parts can even be extended by 1.3-3 times.
Corrosion Resistance
PEEK is chemically inert, and has no reaction to most acids, oils, greases and all other organic and inorganic solvents or enzymes, and can still maintain good strength and dimensional stability.
Self-lubricating
PEEK has low friction coefficient, low running resistance, can be used without oil in some working conditions. The equipment is cleaner, thus improving process reliability, improving energy efficiency and saving costs.
More dom in Design
Injection molds can be used for rapid injection molding of large quantities of complex special-shaped parts, and the cost is low compared to machining.