Item | Standard | Data | Units |
Color | - | Natural | |
Density | ISO 1138 | 1.3±0.01 | g/cm3 |
Water Absorption (25℃.24Hrs) | ISO 62 | 0.05 % | |
Melting temperature | ISO 11357 | 343 | ℃ |
Distortion Temperature | ISO 75-1/-2 | 163 | ℃ |
Continuous service Temperature | UL 74685 | 260 | ℃ |
Thermal expansion coefficient | ASTM D696 | 4.7*10-6 | /K |
Tensile Strength (23℃) | ISO 527 | 100 | MPa |
Tensile modulus (23℃) | ISO 527 | 3.8 | GPa |
Tensile Elongation (23℃) | ISO 527 | 27 % | |
Bending Strength (23℃) | ISO 178 | 163 | MPa |
Bending Modulus (23℃) | ISO 178 | 3.5 | GPa |
Impact Strength(23℃) | ISO 604 | 123 | MPa |
Lzod Impact Strength (No notched) | ISO 180/U | No Break | kJ/m2 |
Poisson Ratio | ISO 527-2 | 0.4 | |
Rockwell Hardness | GB3398.2 | 118 | |
Flammability | UL 94 (1.5 mm) | V-0 | |
Dielectric strength | IEC 60243-1 | 18 | KV/mm |
Dielectric constant | IEC 60250 | 3.2 | |
Thermal Conductivity | ISO 22007 | 0.28 | W/(m·K) |
Surface Resistance | IEC 90093 | 1015 | Ω |
Item | Standard | Data | Units |
Color | - | Black | |
Density | ISO 1138 | 1.4±0.03 | g/cm3 |
Water Absorption (25℃.24Hrs) | ISO 62 | 0.05 % | |
Melting temperature | ISO 11357 | 343 | ℃ |
Distortion Temperature | ISO 75-1/-2 | 315 | ℃ |
Continuous service Temperature | UL 74685 | 260 | ℃ |
Thermal expansion coefficient | ASTM D696 | 1.5*10-6 | /K |
Tensile Strength (23℃) | ISO 527 | 125 | MPa |
Tensile modulus (23℃) | ISO 527 | 9.3 | GPa |
Tensile Elongation (23℃) | ISO 527 | 2.5 % | |
Bending Strength (23℃) | ISO 178 | 271 | MPa |
Bending Modulus (23℃) | ISO 178 | 9.1 | GPa |
Impact Strength(23℃) | ISO 604 | 196 | MPa |
Lzod Impact Strength (No notched) | ISO 180/U | 38 | kJ/m2 |
Poisson Ratio | ISO 527-2 | 0.35 | |
Rockwell Hardness | GB3398.2 | 123 | |
Flammability | UL 94 (1.5 mm) | V-0 | |
Dielectric strength | IEC 60243-1 | - | KV/mm |
Dielectric constant | IEC 60250 | - | |
Thermal Conductivity | ISO 22007 | 0.95 | W/(m·K) |
Surface Resistance | IEC 90093 | 105 | Ω |
Item | Standard | Data | Units |
Color | - | Natural | |
Density | ISO 1138 | 1.5±0.01 | g/cm3 |
Water Absorption (25℃.24Hrs) | ISO 62 | 0.05 % | |
Melting temperature | ISO 11357 | 343 | ℃ |
Distortion Temperature | ISO 75-1/-2 | 315 | ℃ |
Continuous service Temperature | UL 74685 | 260 | ℃ |
Thermal expansion coefficient | ASTM D696 | 2.2*10-6 | /K |
Tensile Strength (23℃) | ISO 527 | 110 | MPa |
Tensile modulus (23℃) | ISO 527 | 7.9 | GPa |
Tensile Elongation (23℃) | ISO 527 | 3.5 % | |
Bending Strength (23℃) | ISO 178 | 214 | MPa |
Bending Modulus (23℃) | ISO 178 | 7.5 | GPa |
Impact Strength(23℃) | ISO 604 | 142 | MPa |
Lzod Impact Strength (No notched) | ISO 180/U | 41 | kJ/m2 |
Poisson Ratio | ISO 527-2 | 0.35 | |
Rockwell Hardness | GB3398.2 | 122 | |
Flammability | UL 94 (1.5 mm) | V-0 | |
Dielectric strength | IEC 60243-1 | 17 | KV/mm |
Dielectric constant | IEC 60250 | 3.4 | |
Thermal Conductivity | ISO 22007 | 0.31 | W/(m·K) |
Surface Resistance | IEC 90093 | 1015 | Ω |
Item | Standard | Data | Units |
Color | - | Black | |
Density | ISO 1138 | 1.44±0.05 | g/cm3 |
Water Absorption (25℃.24Hrs) | ISO 62 | 0.05 % | |
Melting temperature | ISO 11357 | 343 | ℃ |
Distortion Temperature | ISO 75-1/-2 | 315 | ℃ |
Continuous service Temperature | UL 74685 | 260 | ℃ |
Thermal expansion coefficient | ASTM D696 | 2.4*10-6 | /K |
Tensile Strength (23℃) | ISO 527 | 70 | MPa |
Tensile modulus (23℃) | ISO 527 | 4.0 | GPa |
Tensile Elongation (23℃) | ISO 527 | 2.5 % | |
Bending Strength (23℃) | ISO 178 | 100 | MPa |
Bending Modulus (23℃) | ISO 178 | 4.0 | GPa |
Impact Strength(23℃) | ISO 604 | 135 | MPa |
Lzod Impact Strength (No notched) | ISO 180/U | 26 | |
Poisson Ratio | ISO 527-2 | 0.35 | |
Rockwell Hardness | GB3398.2 | 120 | |
Flammability | UL 94 (1.5 mm) | V-0 | |
Dielectric strength | IEC 60243-1 | - | KV/mm |
Dielectric constant | IEC 60250 | - | |
Thermal Conductivity | ISO 22007 | 0.86 | W/(m·K) |
Surface Resistance | IEC 90093 | 105 | Ω |